名称:HJ107
描述:
HJ107 is a fused type no Manganese-oxide flux with granule of bluish gray to dark gray color, about 10-60 mesh in size. This flux is designed for welding of austenitic stainless steel and is of characteristics with less carbon increment and less chromium loss. APPLICATIONS:
This flux is recommended to use with H0Cr21Ni10, H0Cr20Ni10Ti, H00Cr24Ni12Nb, H00Cr21Ni10Nb or H00Cr26Ni12 wires and strips doe welding of stainless steel and anti-corrosion cladding of nuclear pressure vessels and petrol-chemical installations. It is also used for repair welding of high manganese steel with H0Cr16Mn16 wire.
For welding of niobium stabilized stainless steel, the flux of HJ107Nb may be selected to solve the problem of difficult removal of welding slag. TYPICAL PROFERTIES OF CLADDING LAYERS
Being matched with H00Cr26Ni12 (first layer) and H00Cr21Ni10 (surface layers) welding strips for cladding on 50mm thick 18MnMoNb steel. 1.Carbon increment <0.01% Chromium loss <1.5%
2.After sensitization treatment, the specimen has passed the inter-crystalline corrosion test in accordance with GB4334.5-1990 «Method of corrosion test by sulfuric acid-copper sulfate for stainless steel»
GUIDELINES FOR USAGE:
1.Dry the flux at 250ºC ~ 300ºC for 2 hours before use.
2.Completely remove rust, oil and dirt from the groove surface prior to welding. 